Ni-Sn coatings as cathodes for hydrogen evolution in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
In this work the hydrogen evolution reaction (HER) at Ni-Sn alloy coatings, deposited onto Ni 40 mesh at different current densities from the bath containing 0.1 mol dm(-3) SnCl2 + 0.3 mol dm(-3) NiCl2 in the pyrophosphate-glycine ...
The influence of the aging time of RuO2 and TiO2 sols on the electrochemical properties and behavior for the chlorine evolution reaction of activated titanium anodes obtained by the sol-gel procedure
(Elsevier, 2000)
The influence of the aging time of RuO2 and TiO2 sols used for the preparation of (40% RuO2+60% TiO2)/Ti anodes by the sol-gel procedure on the electrochemical properties and behavior for the chlorine evolution reaction ...
Carbon cryogel as support of platinum nano-sized electrocatalyst for the hydrogen oxidation reaction
(Electrochimica Acta, 2006)
The kinetics of hydrogen oxidation reaction was studied in perchloric acid solution on carbon-supported Pt nanoparticles using the rotating disk electrode technique. Carbon cryogel and commercial carbon black. Vulcan XC-72 ...
Hydrogen evolution in acid solution at Pd electrodeposited onto Ti2AlC
(Pergamon-Elsevier Science Ltd, Oxford, 2017)
The hydrogen evolution reaction (HER) was studied in 0.5 M H2SO4 at 25 degrees C on Pd electrodeposited onto Ti2AlC substrate, as an excellent substrate due to its high conductivity and high stability in concentrated ...
Methanol oxidation on an ink type electrode using Pt supported on high area carbons
(Pergamon-Elsevier Science Ltd, Oxford, 2001)
Methanol oxidation was investigated on the following Pt catalysts: bare Pt electrode, Pt covered by nafion (R) film, and pt catalysts supported on high area carbons in the form of an ink. The reaction was carried out using ...
Polarization curves in the ohmic controlled electrodeposition of metals
(Oxford : Pergamon-Elsevier Science Ltd, 2009)
The conditions under which ohmic controlled metal electrodeposition occurs are discussed using a simple mathematical model. it is shown that ohmic controlled electrodeposition can be operative if the value of the exchange ...
Formation of dish-like holes and a channel structure in electrodeposition of copper under hydrogen co-deposition
(Elsevier, 2007)
Copper electrodeposition from acid sulfate solutions at an overpotential of 1000 mV, which is about 250 mV outside the plateau of the limiting diffusion current density, was examined by the determination of the average ...
Nb-TiO2 supported platinum nanocatalyst for oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
Platinum based nanocatalyst at home made Nb-TiO2 support was synthesized and characterized as the catalyst for oxygen reduction reaction in 0.1 mol dm(-3) NaOH, at 25 degrees C. Nb doped TiO2 catalyst support, containing ...
The effect of the electrode surface roughness at low level of coarseness on the polarization characteristics of electrochemical processes
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
In this study, it is considered: (a) the effect of the exchange current density to the limiting diffusion current density ratio (J(0)/J(L)) at low level of surface coarseness on the polarization characteristics of the ...
Oxygen reduction on iron-IV. The reduction of hydrogen peroxide as the intermediate in oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1991)
The kinetics of hydrogen peroxide reduction were studied on iron in borate buffered and unbuffered solutions of pH ranging from 8.6 to 13.8, with and without the presence of chloride ions. A rotating disk electrode was ...