Influence of an accumulative roll bonding (ARB) process on the properties of AA5083 Al-Mg alloy sheets
(Association of Metallurgical Engineers of Serbia AMES, 2014)
In this study, fully annealed AA5083 type alloy sheets with 1 mm in thickness
were processed by accumulative roll bonding (ARB) at room temperature, up to 6 ARB
cycles. It was found that microstructure was refined and ...
Titanium dioxide nanoparticles surface modified with imine as fillers for epoxy resin / Nanočestice titan-dioksida površinski modifikovane iminom kao punioci za epoksidnu smolu
(Univerzitet u Nišu - Tehnološki fakultet, Leskovac, 2018)
The surface of anatase TiO2 nanoparticles was modified with in situ synthesized imine, based on 3,4-dihydroxybenzaldehyde and octadecylamine. The modified TiO2 nanoparticles were investigated using FTIR and UV-Vis spectroscopy, ...
Influence of compression speed and deformation percentage on mechanical properties of calcium alginate particles / Uticaj brzine kompresije i procenta deformacije na mehaničke karakteristike kalcijum alginatnih čestica
(Association of the Chemical Engineers of Serbia, 2015)
Hydrogel particles are often used as carriers for the immobilization of enzymes, polyphenolic antioxidants, whole microbial, plant or mammalian cells. In many processes, the mechanical properties of alginate particles are ...
Synthesis and characterization of semi-interpenetrating networks of chitosan and poly(N-vinyl-2-pyrrolidone) / Sinteza i karakterizacija semi-interpenetrirajućih mreža hitozana i poli(N-vinil-2-pirolidona)
(Association of Chemical Engineers of Serbia, 2010)
Semi-interpenetrating networks (semi-IPNs) based on chitosan and poly(N-vinyl-2-pyrrolidone) were prepared in order to achieve better mechanical properties. The samples were characterized by FTIR, SEM, DMA analysis and the ...
Age hardening potential of an Al-4.6 wt.% Mg alloy with Cu addition
(Belgrade : Institute of Technical Sciences of SASA, 2010)
The ageing behavior of an Al-4.6Mg-0.54Cu (in wt.%) alloy was studied after: (i) solution
treatment for 1h at 530°C, and (ii) annealing at 280°C for 3h. Both groups of the heat treated
specimens underwent further ...