RuOx nanoparticles deposited on TiO2 nanotube arrays by ion-exchange method as electrocatalysts for the hydrogen evolution reaction in acid solution
(Pergamon-Elsevier Science Ltd, Oxford, 2015)
Nanocomposite cathodes for the hydrogen evolution reaction (HER) were prepared by deposition of RuOx catalyst particles on self-organized titania nanotube (TiNT) arrays of highly developed surface area, following a procedure ...
Oxygen reduction reaction on silver electrodes under strong alkaline conditions
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
Oxygen reduction reaction (ORR) was studied on a silver polycrystalline electrode in different NaOH concentrations with a help of rotating disc and rotating ring disc electrodes. Soluble reaction intermediate was detected ...
Voltammetric behavior of erythromycin ethylsuccinate at a renewable silver-amalgam film electrode and its determination in urine and in a pharmaceutical preparation
(Pergamon-Elsevier Science Ltd, Oxford, 2016)
Erythromycin, a macrolide antibiotic, has similar antimicrobial spectrum to penicillin and it is widely used, especially in the treatment of patients who are allergic to penicillin. In this work, the application of a ...
Electrochemical synthesis and characterization of poly(o-toluidine) as high energy storage material
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
Poly(o-toluidine) (POT) is electrochemically synthesized on graphite electrode at constant current density of 1.5 mA cm(-2) from aqueous electrolyte of 1.0 mol dm(-3) H2SO4 and 0.25 mol dm(-3) o-toluidine. Electrochemical ...
Electrooxidative Behavior of Arylazo Pyridone Dyes and Their Inclusion Complexes on Gold Electrode in 0.1 M NaOH
(Pergamon-Elsevier Science Ltd, Oxford, 2014)
The electrochemical behavior of six arylazo pyridone dyes classified to the substituents present at the phenylazo and 2-pyridone moiety and their 1:1 inclusion complexes with (2-hydroxypropyl)-beta-cyclodextrin was studied ...
Service life test of non-noble metal composite cathodes for hydrogen evolution in sodium hydroxide solution
(Pergamon-Elsevier Science Ltd, Oxford, 2012)
In this work polarization characteristics and "service life" test of the non-noble metal composite coatings Ni-MoOx and Ni-MoO2 for hydrogen evolution reaction (HER) in 32 wt.% NaOH at 90 degrees C were investigated and ...
Electrochemical deposition and characterization of Zn-Co alloys and corrosion protection by electrodeposited epoxy coating on Zn-Co alloy
(Pergamon-Elsevier Science Ltd, Oxford, 2002)
Zn-Co alloys electrochemically deposited on steel under various deposition conditions were investigated. The influence of deposition current density, temperature and composition of deposition solution on the phase structure ...
Methanol electrooxidation on supported Pt and PtRu catalysts in acid and alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2002)
The kinetics of methanol oxidation on supported 47.5 wt.% Pt and 54 wt.% Pt-Ru (with nominal Pt:Ru ratios of 2:3) catalysts are measured in 0.5 M H2SO4 and 0.1 NaOH at 295 and 333 K using thin-film rotating disk electrode ...
Voltammetric and differential pulse determination of roxithromycin
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
The oxidative behavior of antibiotic roxithromycin standard was studied at a gold electrode in 0.05 M NaHCO3 using cyclic linear sweep voltammetry and differential pulse voltammetry. It was found that the value of the ...
Comparative studies of chloride and chloride/citrate based electrolytes for zinc-polyaniline batteries
(Pergamon-Elsevier Science Ltd, Oxford, 2006)
Electrochemical behavior of zinc and thin polyaniline (PANI) polymerized from 0.1 M HCl to 0.1 M aniline on graphite electrode, in 0.2 M ZnCl(2) and 0.50 M NH(4)Cl (chloride electrolyte) and with addition of 0.33 M Na-citrate ...