Kinetics of the hydrogen evolution reaction on Fe-Mo film deposited on mild steel support in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2005)
The mechanism and kinetics of the hydrogen evolution reaction were studied. in 1.0 mol dm(-3) NaOH solution on Fe-Mo alloy electrodes prepared by electrodeposition at constant current densities from a pyrophosphate bath. ...
Synthesis and characterization of MoOx-Pt/C and TiOx-Pt/C nano-catalysts for oxygen reduction
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The oxygen reduction reaction (ORR) was studied at carbon supported MoOx-Pt/C and TiOx-Pt nanocatalysts in 0.5 mol dm(-3) HClO4 solution, at 25 degrees C. The MoOx-Pt/C and TiOx-Pt/C catalysts were prepared by the polyole ...
HCOOH oxidation on thin Pd layers on Au: Self-poisoning by the subsequent reaction of the reaction product
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
The oxidation of HCOOH has been investigated on thin Pd layers ranging from 1 to 17 ML equivalents electrodeposited on polycrystalline Au substrate (Pd"Au). The results are compared to those on Pd black. Potentiodynamic ...
Kinetic analysis of hydrogen evolution at Ni-Mo alloy electrodes
(Elsevier Science Ltd, 2000)
The hydrogen evolution reaction (HER) on Ni, Mo and MoNi intermetallic compound was investigated with ac impedance and dc polarization measurements in 1.0 mol dm-3 NaOH solution at 25 °C. The rate constants of the forward ...
Carbon cryogel as support of platinum nano-sized electrocatalyst for the hydrogen oxidation reaction
(Electrochimica Acta, 2006)
The kinetics of hydrogen oxidation reaction was studied in perchloric acid solution on carbon-supported Pt nanoparticles using the rotating disk electrode technique. Carbon cryogel and commercial carbon black. Vulcan XC-72 ...
The influence of the aging time of RuO2 and TiO2 sols on the electrochemical properties and behavior for the chlorine evolution reaction of activated titanium anodes obtained by the sol-gel procedure
(Elsevier, 2000)
The influence of the aging time of RuO2 and TiO2 sols used for the preparation of (40% RuO2+60% TiO2)/Ti anodes by the sol-gel procedure on the electrochemical properties and behavior for the chlorine evolution reaction ...
Ti substrate coated with composite Cr–MoO2 coatings as highly selective cathode materials in hypochlorite production
(Elsevier, 2013)
The aim of this work was to investigate the possibility of preparation of the composite Cr–MoO2 coatings onto steel and titanium substrates as cathode materials with high selective properties which imply the suppression ...
Pt supported on nano-tungsten carbide as a beneficial catalyst for the oxygen reduction reaction in alkaline solution
(Elsevier, 2012)
Platinum nanocatalyst at nano-tungsten carbide was synthesized, characterized and tested for oxygen reduction reaction (ORR) in 0.1 mol dm−3 NaOH, at 25 °C. Tungsten-carbide islands on nano-tungsten particles (WC) was ...
Corrosion protection of mild steel by polypyrrole coatings in acid sulfate solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1997)
The corrosion behaviour of mild steel covered by the electrodeposited polypyrrole films was investigated by electrochemical impedance spectroscopy. Electrodeposition of polypyrrole was performed from aqueous solution of ...
Hydrogen evolution at Zn-Ni alloys
(Pergamon-Elsevier Science Ltd, Oxford, 1998)
Zn-Ni alloys were electrodeposited from a berate-citrate and TEPA bath in potentiostatic and galvanostatic regimes. Potential of electrodeposition or current density were varied and chemical composition and phase structure ...