Crystallization kinetics of K2O·TiO2· 3GeO2 glass studied by DTA
(International Institute for the Science of Sintering, 2008)
Crystallization kinetics of K2O·TiO2· 3GeO2 glass was investigated by differential thermal analysis (DTA). Experiments were performed on powder samples with a particle size < 0.037 mm. The glass samples were heated at ...
Influence of the damage level during quenching on thermal shock behavior of low cement castable
(International Institute for the Science of Sintering, Beograd, 2010)
In the recent decades, the use of unshaped monolithic refractories has been increasing greatly because of their significant advantages over other shaped refractory bricks of the same class. A low cement high alumina castable ...
The effect of Y2O3 addition on thermal shock behavior of magnesium aluminate spinel
(International Institute for the Science of Sintering, Beograd, 2009)
The effect of yttria additive on the thermal shock behavior of magnesium aluminate spinel has been investigated. As a starting material we used spinel (MgAl2O4) obtained by the modified glycine nitrate procedure (MGNP). ...
Improvement of the mechanical properties of spark plasma sintered hap bioceramics by decreasing the grain size and by adding multi-walled carbon nanotubes
(International Institute for the Science of Sintering, Beograd, 2013)
Composites based on HAP and oxidized multi-walled carbon nanotubes (o-MWCNT) and monophase HAP materials were processed by spark plasma sintering. Starting from stoichiometric nano-sized HAP powder, monophase bioceramics ...
Structure and Microstructure Characterization of the La2SrB10O19 Glass-ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
The crystal structure of new lanthanum strontium borate glass-ceramics was refined by the Rietveld method. The results showed that La2SrB10O19 has the monoclinic crystal structure, space group C2 (No. 5) with a = 11.1170(6), ...
Comparison of Morphological Parameters of Ceramic Materials Surface Damage Exposed to Thermal Shock and Cavitation Erosion
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2016)
The surface defects on the samples, which are based on alumina, exposed to thermal shocks and cavitations erosion were analyzed using image analysis. For both types of experimental testing, the samples are made of the same ...
Adsorption of Anthraquinone Dye AB111 from Aqueous Solution using Synthesized Alumina-Iron Oxide Doped Particles
(Science of Sintering, 2021)
Adsorption of anthraquinone dye Acid Blue 111 by alumina-iron oxide doped particles prepared by sol-gel method from aqueous solutions was studied. The adsorbent morphology was revealed by FESEM and the crystallographic ...
Investigation of Possibility for Stabilization and Valorization of Electric Arc Furnace Dust and Glass From Electronic Waste
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2014)
This paper presents investigation of possibility for electric arc furnace dust (EAFD) and electronic waste (e-waste) valorization trough stabilization process, in order to achieve concurrent management of these two serious ...
The Thermophysical Properties of Primary Phase in Lithium Germanium Phosphate Glass
(Science of Sintering, 2021)
The selected lithium germanium-phosphate glass was prepared by a conventional melt-quenching technique. The XRD method was employed to confirm the glass was obtained and to reveal crystalline phases during heat treatment. ...
Characterization of MgAl2O4 Sintered Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
Single phase MgAl2O4 was made from a one-to-one molar ratio of MgO and Al2O3 powders mixed using ball-milling. Mixtures of MgO and Al2O3 were subsequently treated in planetary ball mill for 30, 60, 90 and 120 minutes in ...