Kinetic analysis of hydrogen evolution at Ni-Mo alloy electrodes
(Elsevier Science Ltd, 2000)
The hydrogen evolution reaction (HER) on Ni, Mo and MoNi intermetallic compound was investigated with ac impedance and dc polarization measurements in 1.0 mol dm-3 NaOH solution at 25 °C. The rate constants of the forward ...
Synthesis and characterization of MoOx-Pt/C and TiOx-Pt/C nano-catalysts for oxygen reduction
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The oxygen reduction reaction (ORR) was studied at carbon supported MoOx-Pt/C and TiOx-Pt nanocatalysts in 0.5 mol dm(-3) HClO4 solution, at 25 degrees C. The MoOx-Pt/C and TiOx-Pt/C catalysts were prepared by the polyole ...
The influence of the aging time of RuO2 and TiO2 sols on the electrochemical properties and behavior for the chlorine evolution reaction of activated titanium anodes obtained by the sol-gel procedure
(Elsevier, 2000)
The influence of the aging time of RuO2 and TiO2 sols used for the preparation of (40% RuO2+60% TiO2)/Ti anodes by the sol-gel procedure on the electrochemical properties and behavior for the chlorine evolution reaction ...
Polarization curves in the ohmic controlled electrodeposition of metals
(Oxford : Pergamon-Elsevier Science Ltd, 2009)
The conditions under which ohmic controlled metal electrodeposition occurs are discussed using a simple mathematical model. it is shown that ohmic controlled electrodeposition can be operative if the value of the exchange ...
Oxygen reduction on iron-IV. The reduction of hydrogen peroxide as the intermediate in oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1991)
The kinetics of hydrogen peroxide reduction were studied on iron in borate buffered and unbuffered solutions of pH ranging from 8.6 to 13.8, with and without the presence of chloride ions. A rotating disk electrode was ...
Hydrogen peroxide oxidation on passive iron in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1992)
The kinetics of hydrogen peroxide oxidation were studied on passive iron in alkaline solutions of pH ranging from 9.8 to 13.8, using the rotating disk electrode. Measurements were taken using the linear sweep technique. ...
Kinetics of the hydrogen evolution reaction on Fe-Mo film deposited on mild steel support in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2005)
The mechanism and kinetics of the hydrogen evolution reaction were studied. in 1.0 mol dm(-3) NaOH solution on Fe-Mo alloy electrodes prepared by electrodeposition at constant current densities from a pyrophosphate bath. ...
The effect of the electrode surface roughness at low level of coarseness on the polarization characteristics of electrochemical processes
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
In this study, it is considered: (a) the effect of the exchange current density to the limiting diffusion current density ratio (J(0)/J(L)) at low level of surface coarseness on the polarization characteristics of the ...
Oxygen reduction on iron-Part VI. Processes in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 1994)
The kinetics of oxygen reduction were studied on passivated iron in borate buffered and unbuffered solutions of pH ranging from 7.4 to 13.8. A rotating disk electrode was employed. The O2 reduction on iron under these ...
Ti substrate coated with composite Cr–MoO2 coatings as highly selective cathode materials in hypochlorite production
(Elsevier, 2013)
The aim of this work was to investigate the possibility of preparation of the composite Cr–MoO2 coatings onto steel and titanium substrates as cathode materials with high selective properties which imply the suppression ...