Mechanical properties correlation to processing parameters for advanced alumina based refractories
(International Institute for the Science of Sintering, Beograd, 2012)
Alumina based refractories are usually used in metallurgical furnaces and their thermal shock resistance is of great importance. In order to improve thermal shock resistance and mechanical properties of alumina based ...
Improvement of the mechanical properties of spark plasma sintered hap bioceramics by decreasing the grain size and by adding multi-walled carbon nanotubes
(International Institute for the Science of Sintering, Beograd, 2013)
Composites based on HAP and oxidized multi-walled carbon nanotubes (o-MWCNT) and monophase HAP materials were processed by spark plasma sintering. Starting from stoichiometric nano-sized HAP powder, monophase bioceramics ...
Characterization of dispersion strengthened copper with 3wt%Al2O3 by mechanical alloying
(International Institute for the Science of Sintering, Beograd, 2004)
The copper matrix has been dispersion strengthened with 3wt.%Al2O3 by mechanical alloying. Commercial alumina powder with an average particle size of 0.75mm was used for alloying. The mechanical alloying process was performed ...
Investigation on the Adsorption of the Carbamate Pesticide Methomyl from Aqueous Solution using Modified Co-Beta Zeolite Particles
(International Institute for the Science of Sintering (IISS), 2023)
Adsorption of carbamate pesticide Methomyl by Co-Beta Zeolite particles prepared by wet ion-exchange method from aqueous solutions was studied. The effect of zeolite and pesticide concentrations, pH value, and sintering ...
Influence of sintering temperature on raw and beneficiated clay 'Klokoti'
(International Institute for the Science of Sintering, Beograd, 2012)
The raw clay 'Klokoti' from middle Bosnia was beneficiated by method of wet separation which results in removing fraction over 20 μm. The raw clay was characterized by chemical composition, grain size distribution and ...
Thermal Shock Properties of Glass-ceramics Synthesized From a Glass Frit
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
In this study, the behavior of glass-ceramics synthesized from a glass frit of FFW (Final Flotation Waste) originated from the RTB Bor Company was investigated. Thermal shock resistance was monitored in order to assess the ...
Structure and Microstructure Characterization of the La2SrB10O19 Glass-ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
The crystal structure of new lanthanum strontium borate glass-ceramics was refined by the Rietveld method. The results showed that La2SrB10O19 has the monoclinic crystal structure, space group C2 (No. 5) with a = 11.1170(6), ...
Electrospun Alumina Fibers Doped With Ferric and Magnesium Oxides
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
It is well known that alumina possesses good mechanical and chemical properties. Nanofibers having alpha - alumina structure was used as reinforcement for metal, polymer and ceramic matrix composites. In this study, three ...
Comparison of Morphological Parameters of Ceramic Materials Surface Damage Exposed to Thermal Shock and Cavitation Erosion
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2016)
The surface defects on the samples, which are based on alumina, exposed to thermal shocks and cavitations erosion were analyzed using image analysis. For both types of experimental testing, the samples are made of the same ...
Sol-gel Synthesis of Anatase Nanopowders for Efficient Photocatalytic Degradation of Herbicide Clomazone in Aqueous Media
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
TiO2 nanopowders were produced by sol-gel technique using TiCl4 as a starting material. For the preparation of crystalline anatase with developed surface area, this aqueous solution has been mixed with 0.05 M or 0.07 M ...