Characterization of MgAl2O4 Sintered Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
Single phase MgAl2O4 was made from a one-to-one molar ratio of MgO and Al2O3 powders mixed using ball-milling. Mixtures of MgO and Al2O3 were subsequently treated in planetary ball mill for 30, 60, 90 and 120 minutes in ...
Comparison of Morphological Parameters of Ceramic Materials Surface Damage Exposed to Thermal Shock and Cavitation Erosion
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2016)
The surface defects on the samples, which are based on alumina, exposed to thermal shocks and cavitations erosion were analyzed using image analysis. For both types of experimental testing, the samples are made of the same ...
Influence of Temperature and Different Hydroxides on Properties of Activated Carbon Prepared From Saccharose. Characterization, Thermal Degradation Kinetic and Dyes Removal From Water Solutions
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
In presented paper, influence of temperature, precursor concentration and different hydroxides on properties of activated carbon obtained from saccharose were investigated. The samples were prepared by hydrothermal treatment ...
The Influence of Barium Ferrite Nanoparticles on Morphological and Mechanical Properties of Ethyl Cellulose Based Nanocomposites
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
This study presents preparation and characterization of ethyl cellulose based nanocomposites. Successful use of simple solvent casting technique provided nanocomposites with high loads of barium ferrite magnetic nanopowder ...
Structure and Microstructure Characterization of the La2SrB10O19 Glass-ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
The crystal structure of new lanthanum strontium borate glass-ceramics was refined by the Rietveld method. The results showed that La2SrB10O19 has the monoclinic crystal structure, space group C2 (No. 5) with a = 11.1170(6), ...
Impact of Alumina Particles on the Morphology and Mechanics of Hybrid Wood Plastic Composite Materials
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
Hybrid composite panels of Wood-Plastic Composites (WPC) consisting of wood and poly (methyl methacrylate) (PMMA) were reinforced with alumina particles and made by "hot pressing" method. Alumina-based particles were made ...
Microstructural Characterization and Adsorption Properties of Alkali-Activated Materials Based on Metakaolin
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2016)
The microstructural characterization and adsorption properties of metakaolin (MK) and alkali-activated metakaolin, known as geopolymer materials (GP) were investigated. The structure and properties of the metakaolin and ...
Photocatalytic Degradation of Bisphenol A with alpha-Fe2O3 Fibers and Particles
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2019)
Two-step synthesis of Fe2O3 particles, performed by precipitation from iron(III) chloride (FeCl3 center dot 6H(2)O) using ammonium hydroxide in first step and calcination at 400 and 700 degrees C during 4 h, provided Fe2O3 ...
Final Flotation Waste Kinetics of Sintering at Different Heating Regimes
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2016)
In the copper extraction, especially during the process of flotation enrichment and the pyrometallurgical processing, the waste materials that represent huge polluters of environment are being generated. In order to examine ...
The Effect of the Concentration of Alkaline Activator and Aging Time on the Structure of Metakaolin Based Geopolymer
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2020)
This paper outlines the production of an inorganic polymer/geopolymer using a metakaolin by an environmental friendly, energy saving, clean technology to conserve natural environment and resources. The influence of alkali ...